Evaluation of the effects of zein incorporation on physical, mechanical, and biological properties of polyhydroxybutyrate electrospun scaffold for bone tissue engineering applications

Abstract

Materials and fabrication methods significantly influence the scaffold's final features in tissue engineering. This study aimed to blend zein with polyhydroxybutyrate (PHB) at 5, 10, and 15 wt, fabricate scaffolds using electrospinning, and then characterize them. SEM and mechanical analyses identified the scaffold with 10 wt zein (PHB-10Z) as the optimal sample. Incorporating 10 wt zein reduced fiber diameter from 894 +/- 122 to 531 +/- 42 nm while increasing ultimate tensile strength and elongation at break by approximately 53 and 70 , respectively. FTIR proved zein's presence in the scaffolds and possible hydrogen bonding with PHB. TGA confirmed the miscibility of polymers. DSC and XRD analyses indicated lower crystallinity for the PHB-10Z than for PHB. AFM evaluation indicated a rougher surface for the PHB-10Z in comparison to PHB. The PHB-10Z demonstrated a more hydrophobic surface and less weight loss after 100 days of degradation in PBS than PHB. The free radical scavenging assay exhibited antioxidant activity for the zein-containing scaffold. Eventually, enhanced cell attachment, viability, and differentiation in the PHB-10Z scaffold drawn from SEM, MTT, ALP activity, and Alizarin red staining of MG-63 cells confirmed that PHB-zein electrospun scaffold is a potent candidate for bone tissue engineering applications.