Comparison of the Effects of three Different Surface Treatment Methods with Er: YAG Laser Irradiation on the Bond Strength of Fiber Posts to Resin

Abstract

This study aimed to compare the effect of different surface treatments on the bond strength of fiber posts to composite core material. Thirty light posts were divided into 5 groups. The control group did not receive surface treatment. The H2O2 group was etched with 10 hydrogen peroxide for 20 min, the HF group was etched with 9.5 hydrofluoric acid for 60 sec, the APA group was air abraded with airborne particle abrasion, and the ER group was conditioned with erbiumdoped Yttrium Aluminum Garnet (Er: YAG) laser (250 mJ, 20 Hz, pulse duration of 100 mu s for 1 min). This study aimed to investigate the post -surface preparation by chemical dissolution with materials such as oxygenated water, hydrofluoric acid, or mechanical stress using sandblasting and laser to determine whether these methods lead to increased bond strength. After composite core buildup, each sample was sectioned horizontally to create 1 mm -thick samples. The micro push -out bond strength was evaluated. Data were analyzed by ANOVA, Tukey's post -hoc, and chi-square tests. The significance=0.05. The control and ER groups indicated the minimum and maximum bond strengths respectively. Interface adhesion was significantly improved in the ER and APA groups compared to the H2O2 group. APA and Er: YAG laser (250 mJ, 20 Hz, pulse duration of 100 its for 1 min) were more efficacious than H2O2 in boosting the push -out bond strength of composite resin core material to DT -light fiber post.